Anisoprint CFC PETG
CFC PETG
A material used for coating the composite fiber during continuous
Fiber co-extrusion was developed with the Anisoprint Composer 3D printer
MATERIAL BENEFITS
Reliable binding of fiber layers and load distribution between them ensures
for high strength properties of the resulting composite part.
The molecular structure and properties of the plastic allow it to be filled
possible cavities.
Its low moisture absorption facilitates the process:
CFC-PETG can be printed without prior storage in a dry box.
CHARACTERISTICS
Reinforced with carbon fiber composites (CCF), CFC-PETG 20 times higher tensile strength.
PARAMETER |
CCF-1.5K - PETG |
DENSITY, G/CM3 |
1.4 |
STRENGTH ALONG THE COMPRESSION PATHS, MPA |
774 |
TRAIN MODULE ALONG THE PRESSURE RAILS GPA |
57 |
ELONGATION AT RUPTURE, % |
1.3 |
POINTER CONTRACTION NUMBER 21 |
0.4 |
COMPRESSION PATHS, MPA |
237 |
THE PRESSURE PATHS, GPA |
49 |
COMPRESSIVE ELONGATION, % |
0.52 |
PRINT POLICIES
Make sure you are using the latest version of Aura and Your composer is properly calibrated
before printing.
TEMPERATURE AND COOLING
CFC-PETG is best printed at temperatures between 235 and 245°C.
This plastic is suitable for use in the Composer CFC extruder.
We recommend cooling with fans (50%) to achieve clean fiber division in the CFC process.
SPEED
We recommend 10-20 mm/s for straight fiber paths, these are the standard speeds
in the default aura profiles.
DRYING AND STORAGE
Um eine übermäßige Feuchtigkeitsaufnahme zu vermeiden, lagern Sie das Material an einem kühlen,
trockenen Ort. Die einfachste und sehr effektive Methode ist, Silikagel in die versiegelten
Beutel mit dem Filament zu geben.
CFC-PETG kann ohne Trocknung wochenlang gelagert werden (je nach Luftfeuchtigkeit),
ohne dass die Druckqualität abnimmt. Wenn es etwas Feuchtigkeit aufgenommen hat,
empfehlen wir, das Material in einer Trockenbox zu drucken oder den Kunststoff einfach
4 Stunden lang bei 60 °C zu trocknen.
Material: |
CFC, PETG |
color: |
Transparent |
diameter: |
1,75 mm |
Net weight: |
750 g |